1. Product Overview & Engineering Advantages
Chemically coupled with maleic anhydride (MAH) and 30% glass fibers, this reinforced PP compound achieves a 6,000 MPa flexural modulus, low molding shrinkage, and outstanding lightweight rigidity, widely deployed in automotive structural brackets and heavy-duty furniture hardware.
2. Technical Data Sheet (TDS Specifications)
| Technical Property | Test Method / Standard | Standard Typical Value |
|---|---|---|
| Commercial Grade Name | HuaYing Technical Data | Huaying Lightweight High-Modulus PP+30%GF |
| Product SKU / Code | Internal Identification | HY-PPGF-30 / Code PP+30%GF |
| Polymer Base | TDS Material Type | Chemically Coupled Polypropylene (PP) + 30% Glass Fiber |
| Manufacturing Origin | Production Facility | HuaYing Plants (Binh Duong & Bac Giang) |
| Glass Fiber Content | ASTM D5630 | 30.0 % ± 1.5 % (MAH Coupled) |
| Melt Flow Rate (MFR 230°C/2.16kg) | ASTM D1238 / ISO 1133 | 6.0 g/10min |
| Specific Gravity / Density (23°C) | ASTM D792 / ISO 1183 | 1.14 g/cm³ |
| Tensile Strength at Break | ASTM D638 / ISO 527 | 85.0 MPa |
| Tensile Elongation at Break | ASTM D638 / ISO 527 | 3.2 % |
| Flexural Strength | ASTM D790 / ISO 178 | 125.0 MPa |
| Flexural Modulus | ASTM D790 / ISO 178 | 6,000 MPa |
| Notched Izod Impact Strength (23°C) | ASTM D256 / ISO 180 | 95 J/m (9.5 kJ/m²) |
| Heat Deflection Temp (HDT 1.82 MPa) | ASTM D648 / ISO 75 | 145 °C |
| Molding Shrinkage Rate | ASTM D955 | 0.3 – 0.5 % |
| Environmental Compliance | EDXRF Spectrometer | Compliant with RoHS 2.0 & REACH |
3. Key Industrial Applications
Automotive radiator support brackets, cooling air deflectors, washing machine anti-vibration bases, industrial pump housings, and load-bearing export furniture components.
Representative Global Clients & Certified Partners: Wanek Furniture, Liming Toyota, Shengchang, Noblelift, Tianneng Battery.